Specification
Main material: brass
Color: gold
Melting point: 890℃～905℃
Quantity: 10pcs /
Diameter: 1.6mm / 0.06in
Length: 333mm / 13.1in
Package size:
10pcs: 333 * 7 * 7mm / 13.1 * 0.3 * 0.3in
Package weight:
10pcs: 58.3g / 2.1oz
Â
Note:
1. The weld bevel and the wire surface must be carefully cleaned before welding.
2. Preheating to 400-500℃ before welding. Copper gas welding solvent must be used as a solvent during welding.
3. The welding flame should adopt neutral flame or slight oxidation flame, appropriately reducing the temperature during welding, increasing the welding speed, minimizing the residence time of the molten pool at high temperature, and then can reduce the evaporation and oxidation of zinc.
Package List:
10 * 1.6mm×333mm Brass Welding Wire
20 * 1.6mm×333mm Brass Welding Wire
50 * 1.6mm×333mm Brass Welding Wire (optional)
- No Need Solder Powder - You don't have to use other flux powder with brass as the welding core and coating as the salt base. Very convenient and easy to weld.
- It can weld copper, steel, and hard alloy materials at temperatures ranging from 890℃ to 905℃.
- Light weight, small volume, very easy to carry.
- Good mechanical properties, good wear resistance, excellent fluidity, suitable for temperatureless cold welding.
- Containing a small amount of tin and silicon, tin can improve the fluidity of the wire, and silicon can effectively control the evaporation of zinc.
- No Need Solder Powder - You don't have to use other flux powder with brass as the welding core and coating as the salt base. Very convenient and easy to weld.
- It can weld copper, steel, and hard alloy materials at temperatures ranging from 890℃ to 905℃.
- Light weight, small volume, very easy to carry.
- Good mechanical properties, good wear resistance, excellent fluidity, suitable for temperatureless cold welding.
- Containing a small amount of tin and silicon, tin can improve the fluidity of the wire, and silicon can effectively control the evaporation of zinc.